FH5
flame hardening
Standard Compare
| JUTHA WAN | JIS | AISI/SAE | DIN |
|---|---|---|---|
| FH5 | - | - | - |
Chemical Compounds (%)
C
-
Si
-
Mn
-
Cr
-
Mo
-
V
-
Properties and Applications
• Containing special mixture contributing to capability of Flame Hardening
• Very high hardness obtained after flame hardening
• Mold/die steel suitable for large-sized mold/dies resulting saving repair time of molds/dies
• Used for casting mold/die for forming and cutting work
• Highly capable for producing large-sized vehicle dies
Distribution Formats
• ANNEALED with hardness at 23 HB
Hardening
• Flame Hardening with hardness obtained after hardening at 55-62 HRC
Applications
• Used for casting molds/dies for forming and cutting work
• Highly capable for dies of large-sized vehicles
Standard Compare
| Shape | Specifications |
|---|---|
Flat Bar 
|
flat-shaped steel bar with thickness starting from 32 mm. to 100 mm. (Thickness 32 – 100 mm.) / Width starting from 65 mm. to 305 mm. (Width 65 – 305 mm.) |