SKD11

SKD11

cold work tool steel

Standard Compare
JUTHA WAN JIS AISI/SAE DIN
SKD11 SKD11 D2 1.2379
Chemical Compounds (%)
C
1.50
Si
0.30
Mn
0.40
Cr
12.0
Mo
1.0
V
0.9
C
1.50
Si
0.30
Mn
0.40
Cr
12.0
Mo
1.0
V
0.9

Properties and Applications

• Very high corrosion resistance
• Very deep hardening
• Fair toughness
• Highly capable for hardening
• Capable to be hardened in Vacuum Furnaces
• Maintains long useful life time for cutting edge
• Well resistant to ductility at high temperature
• Very little squeezing occurrence after hardening
• Capable for Nitriding
• Capable for PVD surface treatment

product-kd11s-img02 (1)

Distribution Formats

•  ANNEALED with hardness at 255 HB MIN

 

Hardening

• Hardening temperature at 1000 C – 1040 C. Hardening substances used: oil and air. Hardness  obtained after hardening at 62 HRC
• Tempering temperature at 100C-600C. Hardness obtained after hardening at 50-62 HRC

 

Applications

Widely used in cool work of molding including Blanking molds, Pressing molds, Bending molds, Drawing molds, Cold Extrusion molds, molds used for Trimming and  Coining work, and capable for being used for rolling mills, molds for rolling works, blades for metal and plastic shearing, and molds requiring high corrosion resistance.

Standard Compare
Shape Specifications

เราใช้คุกกี้เพื่อพัฒนาประสิทธิภาพ และประสบการณ์ที่ดีในการใช้เว็บไซต์ของคุณ คุณสามารถศึกษารายละเอียดได้ที่ นโยบายความเป็นส่วนตัว และสามารถจัดการความเป็นส่วนตัวเองได้ของคุณได้เองโดยคลิกที่ ตั้งค่า

Privacy Preferences

คุณสามารถเลือกการตั้งค่าคุกกี้โดยเปิด/ปิด คุกกี้ในแต่ละประเภทได้ตามความต้องการ ยกเว้น คุกกี้ที่จำเป็น

Allow All
Manage Consent Preferences
  • Always Active

Save