Plastic Mold Steel

Plastic Mold Steel

Plastic Mold steel possesses good machinability, weldability and also good mirror polishability. It can also be coated in Nitride or Hard Chrome to increase the abrasion and corrosion resistance and also provide greater lubricity. Coating the steel helps in increasing the durability, weldability and performance of the steel.

Cold Working Tool Steel
JUTHA WAN
JIS
AISI/SAE
DIN
CHARACTER & APPLICATIONS
SPECIFICATION & SIZE RANGE
 
S50C S50C 1049 1.1201 (CM45)
  •  Medium-carbon steel
  •  Good resistance to wear, easily hardened, and possessing high hardness
  •  Being hardened by using NITRIDING for high hardness of surface
  • Used for general moldings, plastic moldings, and a variety of mount metal plates
  •  Capable for producing parts or structure parts of molds
Learn more
P20 PDS-3 P20 1.2311
  • Hardened steel with hardness at 28- 32 HRC
  • Capable for excellently being machined and polished
  • Hardening by NITRIDING and hard chrome plating for better characteristic of surface
  • Steel used to cast molds for plastic works with durability, weldability, and not being fragile
  • Used for casting mold for plastic works requiring high resistance against compressive strength and adhesive  wear
Learn more
KPM30 (Cr-Mo Steel) BETTER THAN P20 1.2311
  • Hardened steel with hardness at 27-33 HRC
  •  Suitable for casting large-sized plastic molds or resin molds
  •  Capable for well and quickly being etched and machined
  • Used for casting molds of vehicle wheel rims, and etc
  • Increasing hardness by hardening with VACUUM NITRIDING providing high surface hardness
Learn more
KPMAX BETTER THAN S55C 1055 CK55
  • Structural adjusted steel by being NORMALIZED with hardness at 28-32 HRC
  • Hardness uniformed and even in all directions of the entire piece of steel
  • Excellent for welding or re-welding
  •  Polishing as mirror and better result of etching
  •  Used for casting special molds and suitable for surface hardening by NITRIDING
Learn more

S50C
JIS
S50C
AISI/SAE
1049
DIN
1.1201 (CM45)
CHARACTER & APPLICATIONS
  •  Medium-carbon steel
  •  Good resistance to wear, easily hardened, and possessing high hardness
  •  Being hardened by using NITRIDING for high hardness of surface
  • Used for general moldings, plastic moldings, and a variety of mount metal plates
  •  Capable for producing parts or structure parts of molds
Learn more
P20
JIS
PDS-3
AISI/SAE
P20
DIN
1.2311
CHARACTER & APPLICATIONS
  • Hardened steel with hardness at 28- 32 HRC
  • Capable for excellently being machined and polished
  • Hardening by NITRIDING and hard chrome plating for better characteristic of surface
  • Steel used to cast molds for plastic works with durability, weldability, and not being fragile
  • Used for casting mold for plastic works requiring high resistance against compressive strength and adhesive  wear
Learn more
KPM30
JIS
(Cr-Mo Steel)
AISI/SAE
BETTER THAN P20
DIN
1.2311
CHARACTER & APPLICATIONS
  • Hardened steel with hardness at 27-33 HRC
  •  Suitable for casting large-sized plastic molds or resin molds
  •  Capable for well and quickly being etched and machined
  • Used for casting molds of vehicle wheel rims, and etc
  • Increasing hardness by hardening with VACUUM NITRIDING providing high surface hardness
Learn more
KPMAX
JIS
BETTER THAN S55C
AISI/SAE
1055
DIN
CK55
CHARACTER & APPLICATIONS
  • Structural adjusted steel by being NORMALIZED with hardness at 28-32 HRC
  • Hardness uniformed and even in all directions of the entire piece of steel
  • Excellent for welding or re-welding
  •  Polishing as mirror and better result of etching
  •  Used for casting special molds and suitable for surface hardening by NITRIDING
Learn more